点击图片查看原图
|
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
||
|
基本性能 |
熔体流动速率 |
230℃/3.8kg |
ASTM D-1238 |
3.3 |
g/10min |
|
物理性能 |
比重 |
|
ASTM D-792 |
1.19 |
g/cm3 |
|
模具收缩率 |
Flow,3.20mm |
ASTM D-955 |
0.50-0.70 |
% |
|
|
机械性能 |
拉伸模量 |
|
ASTM D-638 |
2070 |
MPa |
|
拉伸屈服强度 |
|
ASTM D-638 |
37.8 |
MPa |
|
|
拉伸断裂强度 |
|
ASTM D-638 |
30.3 |
MPa |
|
|
拉伸屈服伸长率 |
|
ASTM D-638 |
2.4 |
% |
|
|
拉伸断裂伸长率 |
|
ASTM D-638 |
17 |
% |
|
|
弯曲模量 |
50.0mm Span |
ASTM D-790 |
2340 |
MPa |
|
|
弯曲屈服强度 |
50.0mm Span |
ASTM D-790 |
67.6 |
MPa |
|
|
IZOD缺口冲击强度 |
23℃ |
ASTM D-256 |
214 |
J/m |
|
|
电气性能 |
体积电阻率 |
|
IEC 60093 |
>1.0E+14 |
ohm.cm |
|
介电强度 |
3.20mm,in Oil |
IEC 60243-1 |
20.00 |
KV/mm |
|
|
热性能 |
热变形温度 |
0.45MPa，未退火，3.20mm |
ASTM D-648 |
86.1 |
℃ |
|
热变形温度 |
1.80MPa，未退火，3.20mm |
ASTM D-648 |
75.0 |
℃ |
|
|
维卡软化温度 |
|
ASTM D-1525 |
93.9 |
℃ |
|
|
CLTE |
Flow,-40TO40℃ |
ASTM E-831 |
0.000090 |
cm/cm/℃ |
|
|
CLTE |
Transverse,-40TO40℃ |
ASTM E-831 |
0.000092 |
cm/cm/℃ |
|
|
燃烧性 |
1.50mm |
UL 94 |
V-0 |
|
|
|
燃烧性 |
2.79mm |
UL 94 |
5VA |
|
|
ABS 沙伯基础FR15U 阻燃抗紫外线